formula Component dosage /g component dosage /g Use The glue is mainly used for bonding metal, organic glass, hard polyvinyl chloride, polystyrene, hard foam and so on. H-703 Epoxy Adhesive formula Component dosage /g component dosage /g Use The glue can be used at 100°C for a long time. It has excellent water and aging resistance and is used for metal and nonmetal bonding. 420# epoxy adhesive formula Component dosage /g component dosage /g Use The glue is used at -55 ~ 82 °C. For adhesive aluminum, steel and other metals and glued epoxy, phenolic, nylon and other plastics and rubber, glass and so on. 204 epoxy adhesive formula Component dosage /g component dosage /g Use The glue is used for metal, wood, glass, fiberglass and other glued joints. 66-04 epoxy adhesive formula Component dosage /g component dosage /g Uses The glue is mainly used for all kinds of rubber and metal, non-metallic products glued. Bonding of glass, ceramics, wood, stone, etc. is also possible. Suitable for use at room temperature. 2000# epoxy resin adhesive formula Component dosage /g component dosage /g Use The glue is used for the bonding of metal and non-metal materials. 2000#(D-17)Epoxy resin adhesive formula Component dosage /g component dosage /g Purpose The adhesive is used for bonding metal and non-metal materials. For rubber products and FRP adhesion is better than the general adhesive. Modified 420 rubber formula Component dosage /g component dosage /g Use This adhesive is used to bond aluminum, steel and other metals and epoxy, phenolic, nylon and other plastics and rubber, glass and so on. HC-1 glue formula Component dosage /g component dosage /g Uses Used for metal, ceramic, hard plastic bonding.
BBQ Grill Mesh is generally made of stainless steel and chrome material. It is resistant to heat, acid, corrosion and wear. Because of these characteristics, it is widely used in the food industry.
If you are a barbecue enthusiast, it must not be without the BBQ Grill Wire Mesh which can help the food to be cooked faster and makes it healthier.
Whether it's meat or vegetables, using BBQ grill mesh can save you time and effort.
XY-921 Epoxy Adhesive
A, 711 epoxy 100 B, 46% cyclohexanone ethanol solution 3.75
Cobalt naphthenate 0.2
Preparation and Curing First prepare the A component and then mix it thoroughly with the B component. Curing at room temperature for 1 to 2 days.
E-51 epoxy resin 100 600# epoxy thinner 10
650# Polyamide 20 Imidazole 8
D-17 polybutadiene epoxy resin 20 β-hydroxyethyl ethylenediamine 8
Preparation and curing According to the amount of weighing in order, can be mixed evenly. This product adhesive pressure is 0.07 ~ 0.15MPa. Cured at 100°C for 3h or 60°C for 4h.
A, E-20 epoxy resin 100 650# polyamide (H-4 curing agent) 140
B-63 epoxy resin 20 B201 coupling agent 3
690# epoxy resin 10 A:B=100:147
B, aluminum oxide (300 mesh) 50
Preparation and curing First, the two components A and B are weighed and mixed according to the amount. When using, re-slurry A, B two components can be evenly proportioned. Cured at room temperature for 24 hours or 80°C for 2 hours.
E-51 epoxy resin 100 650# polyamide 100
Preparation and curing According to the proportion of weighing, mixing can be, at room temperature for 96 hours or 80 °C 3h curing.
E-51 Epoxy Resin 240 Natural Rubber - Methyl Methacrylate Copolymer in Toluene 412
E-44 epoxy resin 240
Toluene 174 acetone A small amount of m-phenylenediamine 70
Preparation and Curing M-phenylenediamine was dissolved in acetone. It is then added to the mixture of the remaining components and mixed well. Cured at 150 °C for 2 h.
D-17 epoxy resin 100 phenylenediamine 2
Hexamethylenediamine 12
Preparation and curing First, the quantitative hexamethylenediamine and m-phenylenediamine were heated and melted, a small amount of epoxy resin was added, and after cooling, the epoxy resin was added. It was cured at 80°C for 2 h, 1201 h, and 150°C for 6 h.
D-17 Epoxy Resin 100 Adipate 60
Preparation and curing Weigh in order and mix evenly. Curing was performed at 100°C for 2 hours, 150°C for 4 hours, and 180°C for 4 hours.
A, E-51 epoxy resin 100 dimethyl benzylamine 5
B-63 epoxy resin 20 coupling agent B201 3
501 Epoxy thinner (propylene oxide butyl ether) 10 Low molecular polysulfide rubber 20
Tricresyl Phosphate 15 Aluminum Oxide (300 mesh) 50
B, 651 Polyamide 100 A: B=100:122.7
Preparation and curing First prepare A, B two components, mixed evenly. 25°C, 50g. The pot life is 4h; 25°C/48h, or 80°C/2h. Curing.
A, epoxy resin 634 100 silane coupling agent B201 3
Glycerin epoxy resin 662 20 Alumina powder (300 mesh) 50
Phenyl glycidyl ether 690 10 A: B=130:193
B. Polyamide resin 650 140
Preparation and curing First, according to the amount of preparation of two components of A, B can be mixed evenly. Curing conditions were 24 h at 25°C, or 2 h at 80°C.